Aung Metals, a well-respected manufacturer and supplier located in Naypyidaw, Myanmar, has built a solid reputation for providing top-notch Stainless Steel 416 Bars and Rods. These products are crafted to offer outstanding machinability, strength, and resistance to corrosion, making them perfect for precision engineering tasks. Aung Metals is committed to upholding international standards and utilizes cutting-edge production methods to ensure consistent quality and performance. Their Stainless Steel 416 Bars and Rods come in a variety of sizes and finishes, tailored to meet the unique needs of industries like automotive, mechanical, and general engineering.
The composition of Stainless Steel 416 Bars and Rods primarily includes chromium (12–14%), carbon (0.15%), along with manganese, silicon, sulfur, and trace elements. The inclusion of sulfur boosts machinability, albeit with a slight compromise on corrosion resistance. These rods boast a tensile strength ranging from 550 to 700 MPa, a yield strength of about 275 MPa, and an elongation of 15%. They deliver impressive mechanical strength and moderate corrosion resistance, and can be heat-treated to enhance hardness and wear resistance, making them ideal for high-performance and precision-engineered components.
Specification : ASTM A276, A479 / ASME SA276, SA479
Standard : EN, DIN, JIS, ASTM, BS, ASME, AISI
Round Bars : Outside Diameter in the range of 4mm to 500mm
Bright Bars : Outside Diameter in the range of 4mm to 100mm
Hex Bars : 18mm – 57mm (11/16″ to 2-3/4″)
Square Bars : 18mm – 47mm (11/16″ to 1-3/4″)
Finish : Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish
Length : 1 to 6 Meters, Custom Cut Lengths
Form : Round, Square, Hex (A/F), Rectangle Etc.
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 416 | 0.15 max | 1.25 max | 1.0 max | 0.06 max | 0.15 min | 14.00 – 12.00 | 0.6 | – | – |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 8.0 g/cm3 | 1454 °C (2650 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35 % |
| STANDARD | WERKSTOFF NR. | UNS | JIS | EN | BS |
| SS 416 | 1.4005 | S41600 | SUS 416 | X12CrS13 | 416S21 |
Stainless Steel 416 is a martensitic stainless steel with a higher level of sulfur and carbon content, which enhances its machinability compared to other stainless steels. This alloy offers improved strength and hardness while still maintaining a good level of corrosion resistance, making it suitable for precision machining.
Yes, Stainless Steel 416 can be heat-treated to increase its hardness. It can be hardened through a quenching and tempering process, which improves its strength, making it ideal for applications that require high wear resistance.
Stainless Steel 416 Bars and Rods are commonly utilized in industries that require high machinability and moderate corrosion resistance. They’re perfect for crafting parts like shafts, gears, bolts, nuts, valves, and pump components. These bars are extensively employed in the automotive, aerospace, and mechanical engineering fields for precision-machined components. Additionally, they are used in food processing equipment, firearms, and instrumentation where strength, hardness, and surface finish are vital. Their blend of toughness, ease of machining, and dimensional stability makes them a go-to choice for a wide range of industrial applications.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Aung Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Naypyidaw, Myanmar